沧州欧谱多种异型冲击装置可以无需校准地自由更换,满足不同客户、不同场合、不同工件精确的硬度测量。
材料 |
硬度制 |
冲击装置 |
|||||
D/DC |
D+15 |
C |
G |
E |
DL |
||
Steel and cast steel 钢和铸钢 |
HRC |
17.9~68.5 |
19.3~67.9 |
20.0~69.5 |
22.4~70.7 |
20.6~68.2 |
|
HRB |
59.6~99.6 |
47.7~99.9 |
37.0~99.9 |
||||
HRA |
59.1~85.8 |
61.7~88.0 |
|||||
HB |
127~651 |
80~638 |
80~683 |
90~646 |
83~663 |
81~646 |
|
HV |
83~976 |
80~937 |
80~996 |
84~1042 |
80~950 |
||
HS |
32.2~99.5 |
33.3~99.3 |
31.8~102.1 |
35.8~102.6 |
30.6~96.8 |
||
Steel锻钢 |
HS |
32.2~99.5 |
|||||
CWT、ST 合金工具钢 |
HRC |
20.4~67.1 |
19.8~68.2 |
20.7~68.2 |
22.6~70.2 |
||
HV |
80~898 |
80~935 |
100~941 |
82~1009 |
|||
HRA |
60.7~92.6 |
||||||
HB |
232~625 |
||||||
Stainless steel 不锈钢 |
HRB |
46.5~101.7 |
|||||
HB |
85~655 |
||||||
HV |
85~802 |
||||||
GC. IRON 灰铸铁 |
HRC |
||||||
HB |
93~334 |
92~326 |
|||||
HV |
|||||||
NC、IRON 球墨铸铁 |
HRC |
||||||
HB |
131~387 |
127~364 |
|||||
HV |
|||||||
C.ALUM 铸铝合金 |
HB |
19~164 |
23~210 |
32~168 |
|||
HRB |
23.8~84.6 |
22.7~85.0 |
23.8~85.5 |
||||
HV |
83.2~648.2 |
||||||
BRASS 铜锌合金 |
HB |
40~173 |
|||||
HRB |
13.5~95.3 |
||||||
BRONZE铜锡(铝)合金 |
HB |
60~290 |
|||||
COPPER纯铜 |
HB |
45~315 |
异型冲击装置 |
DC(D)/DL
|
D+15
|
C |
G |
E |
冲击能量 |
11mJ |
11mJ |
2.7mJ |
90mJ |
11mJ |
冲击体质量 |
5.5g/7.2g |
7.8g |
3.0g |
20.0g |
5.5g |
球头硬度 |
1600HV |
1600HV |
1600HV |
1600HV |
5000HV |
球头直径 |
3mm |
3mm |
3mm |
5mm |
3mm |
球头材料 |
碳化钨 |
碳化钨 |
碳化钨 |
碳化钨 |
金刚石 |
冲击装置直径 |
20mm
|
20mm |
20mm |
30mm |
20mm |
冲击装置长度 |
75mm |
162mm |
141mm |
254mm |
155mm |
冲击装置重量 |
50g |
80g |
75g |
250g |
80g |
试件最大硬度 |
940HV |
940HV |
1000HV |
650HB |
1200HV |
试件表面平均粗糙度Ra |
1.6μm |
1.6μm |
0.4μm |
6.3μm |
1.6μm |
试件最小重量 |
>5kg |
>5kg |
>1.5kg |
>15kg |
>5kg |
可直接测量需稳定支撑 |
2~5kg |
2~5kg |
0.5~1.5kg |
5~15kg |
2~5kg |
0.05~2kg |
0.05~2kg |
0.02~0.5kg |
0.5~5kg |
0.05~2kg |
|
试件最小厚度密实耦合 |
5mm |
5mm |
1mm |
10mm |
5mm |
硬化层最小深度 |
≥0.8mm |
≥0.8mm |
≥0.2mm |
≥1.2mm |
≥0.8mm |
硬度 |
压痕直径 |
0.54mm |
0.54mm |
0.38mm |
1.03mm |
0.54mm |
||||
压痕深度 |
24μm |
24μm |
12μm |
53μm |
24μm |
|||||
硬度 600HV时 |
压痕直径 |
0.54mm |
0.54mm |
0.32mm |
0.90mm |
0.54mm |
||||
压痕深度 |
17μm |
17μm |
8μm |
41μm |
17μm |
|||||
硬度 800HV时 |
压痕直径 |
0.35mm |
0.35mm |
0.35mm |
---- |
0.35mm |
||||
压痕深度 |
10μm |
10μm |
7μm |
10μm |
||||||
沧州欧谱冲击装置 适用范围 |
DC型测量孔或园柱筒内; DL型测量细长窄槽或孔;D型用于常规测量 |
D+15型接触面细小,加长,适宜测量沟槽或凹入的表面 |
C型冲击力小,对被测表面损伤很小,不破坏硬化层, 适合测量小轻薄部件及表面硬化层。 |
G型 测量大厚重及表面较粗糙的铸锻件 |
E型 测量硬度极高材料 |